Go back
PP impact copolymer
AdvyForm E1330
Formerly
Moplen EP140R
Natural
AdvyForm E1330 is a heterophasic copolymer with medium fluidity, for injection moulding and technical compounding. It combines good processability with impact performance, particularly at low temperatures.
Description
AdvyForm E1330 is a heterophasic copolymer with medium fluidity, for injection moulding and technical compounding. It combines good processability with impact performance, particularly at low temperatures. The TDS gives a typical melt flow rate of 22 g/10 min (230 °C/2.16 kg).
Processing Techniques
Supplier-listed processing methods: compounding; injection moulding. Determine processing conditions for the intended application and required properties.
Injection molding
Compounding
Industry and applications
Automotive parts
Compliance and Documentation Notes
Consult the Product Regulatory Summary and Safety Data Sheet (SDS) for regulatory status, including supported, restricted or prohibited applications. Contact Genesis Polymers to request application-specific documentation for AdvyForm E1330.
Technical Properties
Melt Flow Rate
230 °C/2.16 kg
ISO 1133-1
Density
ISO 1183-1
Flexural Modulus
ISO 178
Tensile Modulus
ISO 527-1, -2
Tensile Stress at Break
ISO 527-1, -2
Tensile Stress at Yield
ISO 527-1, -2
Tensile Strain at Break
ISO 527-1, -2
Tensile Strain at Yield
ISO 527-1, -2
Charpy Impact Strength - Notched
23 °C, Type 1, Edgewise, Notch A
ISO 179
Charpy Impact Strength - Notched
0 °C
ISO 179
Charpy Impact Strength - Notched
-20 °C, Type 1, Edgewise, Notch A
ISO 179
Charpy Impact Strength - Notched
-30 °C
ISO 179
Vicat Softening Temperature
A50
ISO 306
Deflection Temperature Under Load
0.45 MPa, Unannealed
ISO 75B-1, -2
Typical values taken from the producer’s (Velogy) technical data sheet, available under Documents. They are not specification limits. Genesis Polymers relies on the producer’s data and cannot accept liability for errors in it. Always check the current data sheet and confirm suitability for your application.
Brand
Feature
High Impact
Supplier documents
Version 1.1, June 2026