Go back
PP random copolymer
AdvyForm R1050
Formerly
Moplen RP225M
Natural
AdvyForm R1050 is a controlled-rheology, medium-modified propylene random copolymer for transparent cast film. It contains slip and antiblocking additives.
Description
AdvyForm R1050 is a controlled-rheology, medium-modified propylene random copolymer for transparent cast film. It contains slip and antiblocking additives. The supplier describes good clarity and gloss, very good processability and very good heat weldability.
Processing Techniques
Supplier-listed processing method: cast film. Determine processing conditions for the intended application and required properties.
Film extrusion
Industry and applications
Food packaging film; stationery film; textile packaging film
Compliance and Documentation Notes
Consult the Product Regulatory Summary and Safety Data Sheet (SDS) for regulatory status, including supported, restricted or prohibited applications. Contact Genesis Polymers to request application-specific documentation for AdvyForm R1050.
Technical Properties
Melt Flow Rate
230 °C/2.16 kg
ISO 1133-1
Density
ISO 1183-1
Flexural Modulus
ISO 527-1, -2
Tensile Stress at Break
23 °C, 50 mm/min
ISO 527-1, -2
Tensile Stress at Yield
23 °C, 50 mm/min
ISO 527-1, -2
Tensile Strain at Break
23 °C, 50 mm/min
ISO 527-1, -2
Tensile Strain at Yield
23 °C, 50 mm/min
ISO 527-1, -2
Charpy Impact Strength
23 °C, Type 1, Edgewise, Notch A
ISO 179
Charpy Impact Strength
0 °C, Type 1, Edgewise, Notch A
ISO 179
Vicat Softening Temperature
A/50
ISO 306
Heat Deflection Temperature B
0.45 MPa, Unannealed
ISO 75B-1, -2
Slip, Erucamide
Velogy method
Antiblock
Velogy method
Typical values taken from the producer’s (Velogy) technical data sheet, available under Documents. They are not specification limits. Genesis Polymers relies on the producer’s data and cannot accept liability for errors in it. Always check the current data sheet and confirm suitability for your application.