PP impact copolymer

KeyForm E1200

""

Natural

Contact Us

PP impact copolymer

Natural

KeyForm E1200

CONTACT

Go back

PP impact copolymer

KeyForm E1200

Formerly

Moplen EP300N

""

Natural

KeyForm E1200 is a heterophasic copolymer for injection moulding. It offers a balance of stiffness, impact strength and processability.

Description

KeyForm E1200 is a heterophasic copolymer for injection moulding. It offers a balance of stiffness, impact strength and processability. Typical uses include packaging, housewares and automotive parts. The TDS gives a typical melt flow rate of 15 g/10 min (230 °C/2.16 kg).

Processing Techniques

Supplier-listed processing methods: compounding; injection moulding. Determine processing conditions for the intended application and required properties.

Injection molding

Compounding

Industry and applications

Crates; housewares; industrial

Compliance and Documentation Notes

Consult the Product Regulatory Summary and Safety Data Sheet (SDS) for regulatory status, including supported, restricted or prohibited applications. Contact Genesis Polymers to request application-specific documentation for KeyForm E1200.

Technical Properties

PROPERTY

VALUE

CONDITIONS

METHOD

Melt Flow Rate

15 g/10 min

15 g/10 min

230 °C/2.16 kg

·

·

ISO 1133-1

Density

0.89 g/cm³

0.89 g/cm³

·

·

ISO 1183-1

Flexural Modulus

1050 MPa

1050 MPa

·

·

ISO 178

Tensile Modulus

1050 MPa

1050 MPa

·

·

ISO 527-1, -2

Tensile Stress at Break

16.5 MPa

16.5 MPa

·

·

ISO 527-1, -2

Tensile Stress at Yield

24 MPa

24 MPa

·

·

ISO 527-1, -2

Tensile Strain at Break

300 %

300 %

·

·

ISO 527-1, -2

Tensile Strain at Yield

7 %

7 %

·

·

ISO 527-1, -2

Charpy Impact Strength - Notched

10 kJ/m²

10 kJ/m²

23 °C, Type 1, Edgewise, Notch A

·

·

ISO 179

Charpy Impact Strength - Notched

5 kJ/m²

5 kJ/m²

0 °C, Type 1, Edgewise, Notch A

·

·

ISO 179

Charpy Impact Strength - Notched

4 kJ/m²

4 kJ/m²

-20 °C, Type 1, Edgewise, Notch A

·

·

ISO 179

Vicat Softening Temperature

148 °C

148 °C

A50

·

·

ISO 306

Deflection Temperature Under Load

78 °C

78 °C

0.45 MPa, Unannealed

·

·

ISO 75B-1, -2

DSC Melting Point

163 °C

163 °C

·

·

DSC

Typical values taken from the producer’s (Velogy) technical data sheet, available under Documents. They are not specification limits. Genesis Polymers relies on the producer’s data and cannot accept liability for errors in it. Always check the current data sheet and confirm suitability for your application.

Brand

KeyForm

Feature

High Impact

High Stiffness

Food Contact

Supplier documents

Technical data sheet (English)

Version 2, June 2026