PP homopolymer
KeyForm P0810
Formerly
Moplen HP552K
Natural
KeyForm P0810 is a polypropylene homopolymer for extrusion of high-tenacity staple fibres. It contains an anti-gas-fading stabilisation package.
Description
KeyForm P0810 is a polypropylene homopolymer for extrusion of high-tenacity staple fibres. It contains an anti-gas-fading stabilisation package. Nonwovens are the supplier's typical application. The TDS gives a typical melt flow rate of 4 g/10 min (230 °C/2.16 kg).
Processing Techniques
Supplier-listed processing methods: continuous filament spinning; fibres; staple fibre. Determine processing conditions for the intended application and required properties.
Fiber nonwoven
Industry and applications
Filament yarn; furniture and buildings; geotextile and agriculture; nonwovens
Compliance and Documentation Notes
Consult the Product Regulatory Summary and Safety Data Sheet (SDS) for regulatory status, including supported, restricted or prohibited applications. Contact Genesis Polymers to request application-specific documentation for KeyForm P0810.
Technical Properties
Melt Flow Rate
230 °C/2.16 kg
ISO 1133-1
Density
ISO 1183-1
Flexural Modulus
ISO 178
Tensile Stress at Break
23 °C, 50 mm/min
ISO 527-1, -2
Tensile Stress at Yield
23 °C, 50 mm/min
ISO 527-1, -2
Tensile Strain at Break
23 °C, 50 mm/min
ISO 527-1, -2
Tensile Strain at Yield
23 °C, 50 mm/min
ISO 527-1, -2
Vicat Softening Temperature
A50
ISO 306
Deflection Temperature Under Load
0.45 MPa, Unannealed
ISO 75B-1, -2
Typical values taken from the producer’s (Velogy) technical data sheet, available under Documents. They are not specification limits. Genesis Polymers relies on the producer’s data and cannot accept liability for errors in it. Always check the current data sheet and confirm suitability for your application.